Glass Filled PEEK
JUTAIPEEK?GF30 is a type of Polymeric Profiles made from 30% of short-cut Glass Fiber Reinforced Polyetherether
Ketone (PEEK). (JUTAIPEEK?GF30V is an extruded profile using VICTREX PEEK Polymers
450GL30 raw materials, and JUTAIPEEK?GF30G is an extruded profile using domestic raw materials).
Compared to PEEK of no-reinforcement, the HDT increases obviously, the strength and modulus increase a
certain extent, and it has better wear-resistance and lower thermal expansion.
This type of products can be applied in the operating condition that is need to bear larger mechanical stress and
wear rate in higher temperature, such as semiconductor production process, precision bearing, tubes and
components in chemical equipment and electrical system.
Product Features
JUTAIPEEK?GF30 type Glass Fiber Reinforced PEEK profiles:
● Good tensile performance, and Tensile Modulus=5-7GPa.
● Good flexural performance, and Flexural Modulus≥6GPa.
● Outstanding thermal mechanical bearing capacity,
and HDT≥250℃.
● Outstanding wear-resistance.
● Outstanding electrical insulation, and dielectric performance.
● Excellent dimensional stability and low thermal expansion.
● High thermal endurance and the long service temperature is 250℃.
Application Fields
JUTAIPEEK?GF30 type Glass Fiber
Reinforced PEEK profiles can be
applied:
—— Mechanical Engineering Industry,；
—— Electrical Industry,；
—— Semiconductor and Electronic
Industry,；
—— Chemical Industry and
Petrochemical Industry.
Instructions for Use
Machined by Lathes or Milling Machine.?
Remove
surface heat-treatment aged layers and the thickness of
removal layer is 0.5-1mm.
Product Storage Instructions
Placed away from light, avoiding humid,
and away from oily substance.
Packed with polymeric film when not use.
Product Technical Data
The performance of JUTAIPEEK
?GF30 series products is as follows:
|
Performance
|
Test Method
|
Unit
|
GF30G
|
GF30V
|
|
Color
|
Eye
|
/
|
Grey-Yellow
|
Grey-Yellow
|
|
Density
|
ISO?1183-1
|
g/cm3
|
1.52
|
1.52
|
|
Tensile Strength
|
ISO 527-2
|
MPa
|
≥105
|
≥110
|
|
Tensile Modulus
|
ISO 527-2
|
GPa
|
≥6
|
≥6
|
|
Elongation At Break
|
ISO 527-2
|
%
|
≥8
|
≥8
|
|
Charpy Impact Strength
|
ISO?179
|
KJ/m2
|
≥4.0
|
≥5.0
|
|
Flexural Strength
|
ISO?178
|
MPa
|
≥200
|
≥205
|
|
Flexural Modulus
|
ISO?178
|
GPa
|
≥7
|
≥6.5
|
|
Rockwell Hardness
|
ISO?2039-2
|
HRM
|
≥100
|
≥100
|
|
Thermal Conductivity
|
ISO?8302
|
W/ (m?K)
|
0.35
|
0.35
|
|
Coefficient of Linear Thermal
Expansion 20-100℃
|
ISO 11359-2
|
10-6/K
|
≤30
|
≤30
|
|
Long Service Temperature
|
UL 746B
|
℃
|
250
|
250
|
|
Heat Deflection Temperature
|
ISO?75-2
|
℃
|
≥250
|
≥250
|
|
Water Absorption （24h）
|
ISO?62
|
%
|
≤0.1
|
≤0.1
|
|
Flame Retardancy
|
UL?94
|
/
|
V-0
|
V-0
|
|
Volume Resistivity
|
IEC?61340-2-3
|
Ω?cm
|
1011-1013
|
1011-1013
|