PEI NATURAL GRADES
JTYPEI?NA is a profile made of pure polyetherimide (PEI) material. PEI is an amorphous polymer with a glass
transition temperature of up to 215°C. It has mechanical properties equivalent to PEEK, as well as excellent heat
resistance, insulation properties, and flame retardancy.
The product can be used in environments with high stress, fatigue stress or impact stress in high temperature
environments, such as auto parts or interior and exterior decoration, semiconductor processing, precision
bearings, mechanical load-bearing components, wind power equipment or new energy battery components,
electrical system.
Product Features
JTYPEI?NA type pure PEI profiles:
● High tensile strength, the strength is above 110MPa.
● High bending strength, the strength is above 150MPa.
● Excellent thermomechanical load-carrying capacity, thermal
deformation temperature is greater than 200℃.
● Good creep resistance and fatigue resistance.
● Excellent flame-retardant performance, low-smoke combustion.
● Excellent dielectric and insulation.
● Excellent dimensional stability, low thermal expansion coefficient.
● High heat resistance, can be used for a long time at 170℃.
● Can transmit microwave.
Application Fields
JTYPEI?NA type PEI profiles can be
applied:
——?Mechanical engineering industry,；
—— Semiconductor and electronics
industry,；
—— Automobile industry,；
——?Home appliance industry.
Instructions for Use
Machined by Lathes or Milling Machine.?
Remove
surface heat-treatment aged layers and the thickness of
removal layer is 0.5-1mm.
Product Storage Instructions
Placed away from light, avoiding humid, and away from oily substance.
Packed with polymeric film when not use.
Product Technical Data
The performance of JTYPEI
?NA series products is as follows:
|
Performance
|
Test Method
|
Unit
|
NA
|
|
Color
|
Eye
|
/
|
Translucent amber
|
|
Density
|
ISO?1183-1
|
g/cm3
|
1.28
|
|
Tensile Strength
|
ISO 527-2
|
MPa
|
≥110
|
|
Tensile Modulus
|
ISO 527-2
|
GPa
|
≥3.1
|
|
Elongation At Break
|
ISO 527-2
|
%
|
≥10
|
|
Notched Charpy Impact Strength
|
ISO?179
|
KJ/m2
|
≥4.0
|
|
Flexural Strength
|
ISO?178
|
MPa
|
≥150
|
|
Flexural Modulus
|
ISO?178
|
GPa
|
≥3.1
|
|
Rockwell Hardness
|
ISO?2039-2
|
HRM
|
≥100
|
|
Glass Transition Temperature
|
ISO?11357-3
|
℃
|
215
|
|
Coefficient of Linear Thermal
Expansion 20-100℃
|
ISO 11359-2
|
10-6/K
|
≤60
|
|
Long Service Temperature
|
UL 746B
|
℃
|
170
|
|
Heat Deflection Temperature
|
ISO?75-2
|
℃
|
≥200
|
|
Water Absorption（23℃,、Water,、24h）
|
ISO?62
|
%
|
≤0.4
|
|
Flame Retardancy
|
UL?94
|
/
|
V-0
|
|
Volume Resistivity
|
IEC?61340-2-3
|
Ω?cm
|
1015-1017
|
|
Dielectric Strength
|
ASTM?D149-20
|
kV/mm
|
≥26
|
|
Dielectric Constant
|
IEC?62631-2-1
|
1
|
3.4
|
|
Dielectric Loss
|
IEC?62631-2-1
|
1
|
5.44*10-3
|